Specification |
|
E2 |
|
Description |
|
Thick new production steel scrap predominantly more than 3 mm thick prepared in a manner to ensure direct charging. The steel scrap must be uncoated unless permitted by joint agreement and be free of rebars and merchant bars even from new production. Must be free of metallic copper, tin, lead (and alloys), mechanical pieces and steriles to meet the aimed analytical contents. |
|
Dimensions |
|
Thickness 3 mm Dimension 1,5x0,5x0,5 m |
|
Density(t/m³) |
|
0,6 |
|
Steriles* |
|
< 0,3% |
|
|
|
|
Specification |
|
E8 |
|
Description |
|
Thin new production steel scrap predominantly less than 3 mm thick prepared in a manner to ensure direct charging. The steel scrap must be uncoated unless permitted by joint agreement and be free of unbound ribbons to avoid trouble when charging. Must be free of metallic copper, tin, lead (and alloys), mechanical pieces and steriles to meet the aimed analytical contents. |
|
Dimensions |
|
Thickness 3 mm Dimension 1,5x0,5x0,5 m (except bound ribbons) |
|
Density(t/m³) |
|
0,4 |
|
Steriles* |
|
< 0,3% |
|
|
Specification |
|
E6 |
|
Description |
|
New production thin steel scrap (less than 3 mm thick) compressed or firmly baled in a manner to ensure direct charging. The steel scrap must be uncoated unless permitted by joint agreement.Must be free of metallic copper, tin, lead (and alloys), mechanical pieces and steriles to meet the aimed analytical contents. |
|
Dimensions |
|
|
|
Density(t/m³) |
|
1 |
|
Steriles* |
|
< 0,3% |
|
|
* Corresponds to the weight of steriles, not adhering to the scrap, remaining at the bottom of the vehicle after unloading by magnet. |
|
|
|
|
|
|
|
|
|
|
|
|
|